Veneziani Ticoprene AL Aluminised Primer 2.5Lt 473COL2218

MORE INFORMATION

CHLORINATED RUBBER PRIMER

BARRIER COAT
EXCELLENT PROTECTION AND ADEHSION
HIGH IMPERMEABILITY
EASY TO APPLY

FEATURES
Ticoprene is a one-component chlorinated rubber primer pigmented with aluminium flakes, an all-purpose primer for the marine environment, suitable for maintenance painting of wood and steel boat hulls and structures. It can be applied also to zinc primers as well as to one-component and two-component primers. Well suited as a sealer for old antifoulings. Ticoprene provides good protection to parts immersed in salt and fresh water.

TECHNICAL DATA
Curing mechanism: thinner evaporation
Specific weight: 1.26 ± 0.02 kg / l
Volume solids: 32%
Flash point: +26 ° C
Appearance: matt
Colour: aluminium

SURFACE PREPARATION
All substrates to be painted must be clean, dry and free of any contamination.
New and stripped wood : the humidity content must be below 18%. Sand with 100-120 grade paper and blow with dry compressed air. Apply 1 coat of Ticoprene diluted with 25% thinner 6470. After drying apply 2 or 3 additional coats of Ticoprene.
Steel: Sand with 80-100 grade paper and blow with dry compressed air. Apply 3 coats of Ticoprene. As a sealing coat for old and unknown antifoulings: high pressure washing and subsequent sanding.

APPLICATION
Stir the paint for 5 minutes with a power mixer until the colour is even. The paint is ready for brush or roller application. If necessary, up to 5% thinner 6470 may be added. For spray application up to 10% thinner 6470 may be added. Apply an even coat using criss-cross strokes. For best results, the paint should be applied when the temperature of the substrate is above 7° C. In any case the temperature of the substrate shall be at least 2° C above the dew point.

APPLICATION DATA
Drying time before use(20 ° C): 24 hours
Pot life (20 ° C):                  /
Application temperature min / max: + 5 / + 35 ° C
Hardener:                           /
Mixing ratio by volume:       /
Mixing ratio by weight:        /
Thinner: 6470
Wet film thickness per coat: 150 microns
Dry fllm thickness per coat: 50 microns
Theoretical coverage: 5,3 m2/L
Recoating time at 20°C at least 12 hours maximum /
Number of coats: 1 to 4

Data for spray application:
Nozzle diameter: Conventional: 1.7 / 2.2 mm. Airless: 0.017 / 0.023 inch.
Air Pressure: Conventional: 3.5 / 4.5 atm. Airless: /
Compression ratio: Conventional: /
Airless: 30: 1